Brians Questions:
I have a question that i would like your input on. I have a double car garage that i use as my workshop. I want to build an outfeed table for my tablesaw. I was thinking of something that could be multi use. I was thinking of making two 2’x 4′ workbenches that would be on hinges so i could open it as a 2×8 or close it so its 4×4. I was thinking of using castors as well as adjustable feet. Im not 100% sold on the idea and was just hoping to hear some suggestions from the pros!
Hopefully this makes for a good question for your podcast.
Once again, thank you for the AMAZING podcast and youtube videos.
Matt
Hi all,
First, thanks for the podcast, by far the best format and the best information. It seems each podcast I almost always learn something.
I have a question about glue ups. When I glue up a joint, I try to keep squeeze out to a minimum and by doing that I’m not sure if I’ll use enough glue. However, squeeze out is inevitable. Do you try to keep squeezing out to a minimum and if so what steps do you take. Also, when you do have squeeze out on a joint what do you do to get rid of the excess glue. I’m not talking about squeeze out on a panel, since it’s easy to either use a plane to get rid of the glue when it dries, or sand it away. Any advice that you could share would be greatly appreciated.
Thanks, Mike
Guys Questions:
Hello! My name is Eric. I am a rather new/inexperienced woodworker. After hurricane Helene did so much damage in South Carolina, I decided I no longer wanted a large Hickory tree beside my house.
I paid professionals to fell this 100 year-old tree. I paid my friend, a rookie, to mill it into 5/4 inch planks/boards. I’ve been air-drying this wood in my garage for over a year. It is time to do something with it.
When I looked up, “What should you make out of Hickory?” The answers are baseball bats, ax handles, hardwood floors, and steps for staircases. I am not going to make any of those.
I have 750 board foot of this stuff…
What should I make?
What should I not make with this wood?
What gotchas do I need to be prepared for?
Any other advice?
Eric in SC
Hi guys,
I’m building a large frame for a canvas artwork for a friend. I’d like to reinforce the miters using miter keys.
Previously, I’ve cut the slots for miter keys on the table saw with a dedicated 45 degree jig when building small boxes. This frame is pretty big though, and I think the size would make it really awkward to do this way on the table saw.
Any other methods besides the table saw you’ve had success with cutting miter keys? Do you have any general recommendations for thickness of the miter keys in relation to the miter itself? Or at what thickness of material you would consider multiple miter keys for added strength? The frame is all going to be stained the same color so I’m not worried about aesthetic of the keys or contrasting with different wood species, just purely doing it for added strength. The frame is 1.5” thick with 4/4 ash and about 3 feet by 5 feet for reference.
Thanks! Evan
Huys Questions:
The veneers were shopsawn in house and are 1.8mm – 2.4mm with some of the walnut 5000mm long and 600mm wide the species also include.
- Walnut burl.
- Yellow poplar burl.
-Maple - Pacific maple.
- European Walnut
- European oak
- Silky Oak
- QLD Pepperwood
- Palisander Rosewood
- Tasmanian blackwood
- Fiddleback Tasmanian Blackwood
- Blackbutt
My other question is, can the three of you suggest a project each of small to medium size I can do with this veneer . I find it easier to work towards something when I have been told what to do rather than racking my brain in the workshop trying to think of something to do whilst drowning in a sea of veneer.
Dylan
Hi folks
First as always thanks for one of the most friendliest and informative woodworking podcasts.
So here’s my dilemma. I’ve often heard about letting the wood acclimate to your shop environment before beginning a project. I understand that. My confusion comes in when starting to mill the wood. It’s often mentioned to mill the wood in graduated steps of a couple of days to allow it to release any built up tension. However I never hear of this being done in large production shops. Guy and Brian how do you do this where you work?
Thanks, Doug